Titanium
Titanium CP
Grade 2
Grade 2 titanium is the most popular and widely-available of the four commercially pure grades. It has similar corrosion resistance and formability to Grade 1, but with higher strength.
Key benefits
- Corrosion resistance
- Formability
- Weldability
Standards
- ASTM F67
- ISO 5832-2
Forms available in stock
Diameter
- 0.4 mm to 100 mm
Length
- 3000 mm approx.
Thickness
- 0,4 mm to 60 mm
Dimensions
- Width 1000 to 2000 mm
- Length 1000 to 6000 mm
Diameter
- 0,32 mm to 10 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Thickness
- from 3 mm
Width
- from 10 mm
Length
- up to 6000 mm
Standards
- ASTM B348
- ASME SB348
- ASTM B265
Forms available in stock
Diameter
- 0.4 mm to 300 mm
Length
- 3000 mm approx.
Thickness
- 0,4 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 0.32 mm to 10 mm
Hexagonal head screw
- DIN 931/933
Hexagonal hollowed cylindric screw
- DIN 912
Hexagonal hollowed milled head screw
- DIN 7991
Cylindric split head screw
- DIN 84
Cylindric split crowned head screw
- DIN 85
Split milled head screw
- DIN 963
Split crowned head screw
- DIN 964
Headless hexagonal hollowed screw
- DIN 913
Threated rod - Standard length : 1 meter
- DIN 975
Hexagonal nuts/Brake/Collar
- DIN 934
- DIN 985
Washer
- DIN 125
- DIN 127
Stud
- DIN 938
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Thickness
- from 3 mm
Width
- from 10 mm
Length
- up to 6000 mm
Forms available on demand
Thickness
- From 100 mm
Width
- On demand
Standards
- ABS 5142A
- AIMS 03-18-002
- AMS 4902
- ASNA 3201
- WL 3.7034.1
- LN 9297
- ASTM B265
Forms available in stock
Thickness
- 0,4 mm to 3 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Chemical composition
Reference standard : ASTM B348
Fe
- 0% min
- 0.3% max
O
- 0% min
- 0.25% max
N
- 0% min
- 0.03% max
C
- 0% min
- 0.08% max
H
- 0% min
- 0.015% max
Other (each)
- 0% min
- 0.1% max
Other (total)
- 0% min
- 0.4% max
Ti
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
345
Rp 0,2 (Mpa)
275
Density (g/cm3)
4.51
A (%)
18%