Titanium
Grade 5
TA6V
Ti6Al4V grade 5 is an alpha-beta titanium alloyed with aluminium and vanadium. It offers an excellent compromise between mechanical resistance, toughness and ductility. Furthermore, its machinability makes it easy to weld.
Key benefits
- Corrosion resistance
- Formability
- Weldability
Standards
- ASTM F1472
- ISO 5832-3
Forms available in stock
Diameter
- 8 mm to 100 mm
Length
- 3000 mm approx.
Dimensions
- Any kind of granulometry suitable to your machine
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Standards
- ASTM B348
- ASTM B265
Forms available in stock
Diameter
- 10 mm to 260 mm
Length
- 3000 mm approx.
Thickness
- 5 mm to 60 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Hexagonal head screw
- DIN 931/933
Hexagonal hollowed cylindric screw
- DIN 912
Hexagonal hollowed milled head screw
- DIN 7991
Cylindric split head screw
- DIN 84
Cylindric split crowned head screw
- DIN 85
Split milled head screw
- DIN 963
Split crowned head screw
- DIN 964
Headless hexagonal hollowed screw
- DIN 916
Threated rod
- Standard length : 1 meter
- DIN 975
Hexagonal nuts/Brake/Collar
- DIN 934
- DIN 985 (brake)
Washer
- DIN 125
- DIN 127 (brake)
Stud
- DIN 938
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Forms available on demand
Thickness
- From 100mm
Width
- On demand
Standards
- AMS 4911
- AMS 4928
- ASTM B265
- ABS 5326C
- AIMS 03-18-006
- ASNA 3200
- ABS 5125A
- AIMS 03-18-001
- ASNA 3304
- WL 3.7164.1
- LN 9297
- ABS 5453A
- ASNA 3307
- ABS 5125B
- ABS 5125C
Forms available in stock
Diameter
- 6 mm to 320 mm
Length
- 2000 to 4000 mm around
Thickness
- 0,4 mm to 110 mm
Width
- 1000 to 2000 mm
Length
- 1000 to 6000 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Diameter
- 3 to 50.8 mm
Thickness
- 0.3 to 5 mm
Forms available on demand
Thickness
- According to plans
Width
- According to plans
Chemical composition
Reference standard : ASTM B348
Fe
- 0% min
- 0,4% max
O
- 0% min
- 0,2% max
N
- 0% min
- 0,05% max
C
- 0% min
- 0,08% max
H
- 0% min
- 0,015% max
Al
- 5,5% min
- 6,75% max
V
- 3,5% min
- 4,5% max
Ti
- —
- Balance
Back
Mechanical properties
Rm (Mpa)
895
Rp 0,2 (MPA)
828
Density (g/cm3)
4,43
A (%)
10