Titanium

Titanium CP
Grade 1

Grade 1 titanium offers the best ductility and formability of the four commercially pure grades, as well as excellent corrosion resistance in oxidising or moderately reducing environments, including chlorides. It has good toughness even at low temperatures and can be easily welded, machined and deformed at hot and cold temperature.

Key benefits

  • Corrosion resistance

  • Formability

  • Weldability

Standards

  • ASTM F67

  • ISO 5832-2

Forms available in stock

Diameter
  • 0.4 mm to 100 mm
Length
  • approx. 3000 mm
Thickness
  • 0,4 mm to 60 mm
Dimensions
  • Width 1000 to 2000 mm
  • Length 1000 to 6000 mm
Diameter
  • 0,32 mm to 10 mm
Diameter
  • 3 to 50.8 mm
Thickness
  • 0.3 to 5 mm
Diameter
  • 3 to 50.8 mm
Thickness
  • 0.3 to 5 mm
Thickness
  • From 3 mm
Width
  • From 10 mm
Length
  • Up to 6000 mm

Standards

  • ASTM B348

  • ASME SB348

  • ASTM B265

Forms available in stock

Diameter
  • 0.4 mm to 300 mm
Length
  • approx. 3000 mm
Thickness
  • 0,4 mm to 60 mm
Width
  • 1000 to 2000 mm
Length
  • 1000 to 6000 mm
Diameter
  • 2 mm to 10 mm
Diameter
  • 3 to 50,8 mm
Thickness
  • 0,3 to 5 mm
Diameter
  • 3 to 50,8 mm
Thickness
  • 0,3 to 5 mm
Thickness
  • from 3 mm
Width
  • from 10 mm
Length
  • up to 6000 mm

Forms available on demand

Thickness
  • From 100 mm
Width
  • On demand

Standards

  • DIN 65039

  • LN 9297

  • ASTM B265

  • WL 3.7024.1

Forms available in stock

Diameter
  • 0.4 mm to 300 mm
Length
  • approx. 3000 mm
Thickness
  • 0,4 mm to 60 mm
Width
  • 1000 to 2000 mm
Length
  • 1000 to 6000 mm
Diameter
  • 0,32 mm to 10 mm
Diameter
  • 3 to 50,8 mm
Thickness
  • 0,3 to 5 mm
Diameter
  • 3 to 50,8 mm
Thickness
  • 0,3 to 5 mm
Thickness
  • from 3 mm
Width
  • from 10 mm
Length
  • up to 6000 mm

Chemical composition

Norm of reference : ASTM B348
Fe
  • 0% min
  • 0,2% max
O
  • 0% min
  • 0,18% max
N
  • 0% min
  • 0,03% max
C
  • 0% min
  • 0,08% max
H
  • 0% min
  • 0,015% max
Other (each)
  • 0% min
  • 0,1% max
Other (total)
  • 0% min
  • 0,4% max
Ti
  • Balance
Back

Mechanical properties

Rm (Mpa)
240
Rp 0,2 (Mpa)
170
Density (g/cm3)
4,51
A (%)
25