Titanium

Grade 9
Ti3Al-2.5V

Grade 9 titanium offers a better weldability, mechanical resistance and formability than TA6V. This metal is mainly used in aerospace but also for bicycle frames and golf clubs.

Key benefits
  • Weldability
Standards
  • ISO 15156
  • NACE MR0175
  • ASTM B265
  • ASTM B337
  • ASTM B338
  • ASTM B348
  • ASTM B381
  • ASTM B861
  • ASTM B862
Forms available on demand
Diameter
  • 0.4 mm to 300 mm
Length
  • 3000 mm approx.
Thickness
  • 0,4 mm to 60 mm
Width
  • 1000 to 2000 mm
Length
  • 1000 to 6000 mm
Diameter
  • 2 mm to 10 mm
Diameter
  • from 3 to 50,8 mm
Thickness
  • from 0,3 to 5 mm
Diameter
  • from 3 to 50,8 mm
Thickness
  • from 0,3 to 5 mm
Standards
  • AMS 4943
  • AMS 4944
Forms available on demand
Diameter
  • 0.4 mm to 300 mm
Length
  • 3000 mm approx.
Thickness
  • 0,4 mm to 60 mm
Width
  • 1000 to 2000 mm
Length
  • 1000 to 6000 mm
Diameter
  • 0,32 mm to 10 mm
Diameter
  • from 3 to 50,8 mm
Thickness
  • from 0,3 to 5 mm
Diameter
  • from 3 to 50,8 mm
Thickness
  • from 0,3 to 5 mm

Chemical composition

O
  • 0% min
  • 0,15% max
N
  • 0% min
  • 0,03% max
C
  • 0% min
  • 0,08% max
H
  • 0% min
  • 0,015% max
Fe
  • 0% min
  • 0,25% max
Al
  • 2,5% min
  • 3,5% max
V
  • 2,0% min
  • 3,0% max
Ti
  • Balance
Back

Mechanical properties

Rm (Mpa)
620
Rp 0,2 (Mpa)
483
Density (g/cm3)
4,48
A (%)
15
Z %
25