Stainless steel

17-4 PH
1.4542
AISI 630
Cond. H 1050

17-4PH is a precipitation-hardened martensitic stainless steel, used for pieces which require high mechanical strength, important resilience and also good fatigue resistance. This metal is remelted by using the ESR method in order to combine a good homogeneity and structural isotropy with excellent mechanical properties (longitudinal and transversal direction).

Avantages
  • Excellent mechanical properties
  • Very resilient
  • Multipurpose alloy
PDF

Plus d'info sur
17-4 PH
1.4542
AISI 630
Cond. H 1050

Contactez nous + 33 (0)4 72 14 55 00
Normes
  • ASTM A564
  • ASTM F899
  • EN 10088-3
  • NFS94-090
Formes disponibles en stock
Diameter
  • 5 mm à 110 mm
Length
  • 3000 mm around
Granulometry
  • Every granulometry according to your machine
Diameter
  • 3 à 50.8 mm
Thickness
  • 0.3 à 5 mm
Diameter
  • 3 à 50.8 mm
Thickness
  • 0.3 à 5 mm
Formes disponibles sur demande
Thickness
  • On demand
Dimensions
  • On demand
Normes
  • AMS 5643
  • ASTM A564
  • Cond H1025
  • Cond H1150
Formes disponibles en stock
Diameter
  • 25 à 200 mm
Length
  • 3600 à 4000 mm

Composition chimique

C
  • 0% min
  • 0,06% max
Mn
  • 0% min
  • 0,7% max
Si
  • 0% min
  • 0,7% max
P
  • 0% min
  • 0,025% max
S
  • 0% min
  • 0,015% max
Cr
  • 15% min
  • 17% max
Ni
  • 305% min
  • 5% max
Nb
  • 5xC% min
  • 0,45% max
Cu
  • 3% min
  • 4,5% max
Mo
  • 0% min
  • 0,5% max
Fe
  • Balance
  • -
Haut de page

Caractéristiques mécaniques

Rm (Mpa)
≥ 930
Rp 0,2 (Mpa)
≥ 725
Density (g/cm3)
7.8
A (%)
≥ 16